Toteutusstandardit: GB/T8162 saumaton teräsputki rakenteisiin, GB/T8163 saumaton teräsputki nesteen kuljetukseen. 0420D ja 0420E mekaaniset ominaisuudet: vetolujuus 520 ~ 680 MPa,<16 service strength 2420MPa, 16mm~30mm service strength 2400, 230mm Yield strength 2380MPa Impact test Q420D minus 20C Impact energy 234, impact test Q420E minus 40C Impact energy 227 :0.20, chromium: <0.30, nickel: <0.50, copper: 0.20, nitrogen: 0.015, :0.20, aluminum, 20.015.Q420E seamless steel pipe chemical composition: carbon: 0.20, silicon: 0.50, :1.70, phosphorus: 0.025, Sulfur: 0.020, : 0.07, : 0.20, : 0.20 Chromium: <0.30, Nickel: <0.50, Copper: <0.20, Nitrogen: 0.015, : 0.20, Aluminum, 20.015. Steel refining method: Steel should be processed by electric arc furnace Refining outside the furnace or gas converter plus outside refining method. After negotiation between the supply and demand parties, other methods with higher requirements can also be used to treat refining. When the demander requires a certain refining method, it should be stated in the contract.
Putken valmistusmenetelmä: Putket voidaan valmistaa myös jatkuvalla valulla, muottivalulla tai kuumavalssaamalla.
Jatkuvavalettujen putkien tulee myös täyttää YB/T 4149:n määräykset; kuumaputkien tulee myös täyttää YB/T 5221 tai YB/T 5222 määräykset; muottivaletut putket voivat viitata myös kuuman (taotun) putkien määräyksiin.